    Effect of deposition strategy and post processing on microstructure and mechanical properties of serviced Inconel 625 parts repaired using laser directed energy deposition
    (Elsevier Ltd, 2024) Chaurasia, J.K.; Jinoop, A.N.; Paul, C.P.; Bindra, K.S.; Balla, V.K.; Bontha, S.
    In the present work, an attempt is made to understand and explore the repair capabilities of the Laser Directed Energy Deposition (LDED) process on Nickel based superalloy Inconel 625 (IN625). Samples were extracted from a wrought plate of IN625 and then were subjected to a fatigue test to mimic a component in service for repairing. Further, deposition was carried out on these fatigued tensile sample surfaces i.e., Top, Top & bottom, One side and Both sides. The samples were also solution-treated at 1200 °C for 90 mins. Microstructure and mechanical properties were evaluated and then compared between the different deposition strategies and sample heat-treatment conditions. Tensile properties were compared for all the three sample conditions viz. wrought alloy, as repaired and solution treated. Results indicate sound deposition with minimal porosity in all the four deposition strategies using the LDED process with a mean deposit height of 1.02 ± 0.25 mm. Microstructural analysis revealed mixed dendrite and columnar structure in the case of as-deposited samples whereas, solution treated samples exhibited recrystallized equiaxed grains with the presence of annealing twins. The as-deposited samples show a ductile mode of failure with a maximum ultimate strength of 830 MPa, yield strength of 350 MPa and elongation of 72%. For solution treated samples, a maximum ultimate tensile strength of 620 MPa, yield strength of 270 MPa and elongation of 73% were observed. The strength of the material was found to be highly influenced by the solution treatment. © 2023 Elsevier Ltd
  • No Thumbnail Available
    Item
    Enhancing fatigue performance of AZ31 magnesium alloy components fabricated by cold metal transfer-based wire arc directed energy deposition through LPB
    (KeAi Communications Co., 2024) Manjhi, S.K.; Bontha, S.; Balan, A.A.S.
    Cold Metal Transfer-Based Wire Arc Directed Energy Deposition (CMT-WA-DED) presents a promising avenue for the rapid fabrication of components crucial to automotive, shipbuilding, and aerospace industries. However, the susceptibility to fatigue of CMT-WA-DED-produced AZ31 Mg alloy components has impeded their widespread adoption for critical load-bearing applications. In this study, a comprehensive investigation into the fatigue behaviour of WA-DED-fabricated AZ31 Mg alloy has been carried out and compared to commercially available wrought AZ31 alloy. Our findings indicate that the as-deposited parts exhibit a lower fatigue life than wrought Mg alloy, primarily due to poor surface finish, tensile residual stress, porosity, and coarse grain microstructure inherent in the WA-DED process. Low Plasticity Burnishing (LPB) treatment is applied to mitigate these issues, which induce significant plastic deformation on the surface. This treatment resulted in a remarkable improvement of fatigue life by 42%, accompanied by a reduction in surface roughness, grain refinement and enhancement of compressive residual stress levels. Furthermore, during cyclic deformation, WA-DED specimens exhibited higher plasticity and dislocation density compared to both wrought and WA-DED + LPB specimens. A higher fraction of Low Angle Grain Boundaries (LAGBs) in WA-DED specimens contributed to multiple crack initiation sites and convoluted crack paths, ultimately leading to premature failure. In contrast, wrought and WA-DED + LPB specimens displayed a higher percentage of High Angle Grain Boundaries (HAGBs), which hindered dislocation movement and resulted in fewer crack initiation sites and less complex crack paths, thereby extending fatigue life. These findings underscore the effectiveness of LPB as a post-processing technique to enhance the fatigue performance of WA-DED-fabricated AZ31 Mg alloy components. Our study highlights the importance of LPB surface treatment on AZ31 Mg components produced by CMT-WA-DED to remove surface defects, enabling their widespread use in load-bearing applications. © 2024