Faculty Publications
Permanent URI for this communityhttps://idr.nitk.ac.in/handle/123456789/18736
Publications by NITK Faculty
Browse
4 results
Search Results
Item Microstructural characterization of low temperature plasma-nitrided 316L stainless steel surface with prior severe shot peening(Elsevier Ltd, 2016) Jayalakshmi, M.; Huilgol, P.; Badekai Ramachandra, B.R.; Bhat, K.U.Surface nanocrystallization by severe deformation has proven beneficial as pre-treatment to plasma nitriding. It aids in achieving thicker nitride layers at lower temperatures thus making the process more economical. In austenitic stainless steels, severe deformation leads to formation of strain induced martensite on the surface while plasma nitriding alone forms expanded austenite. However, structural characteristics of surface layer of pre-deformed steel after plasma nitriding is still a matter of debate. In present study, 316L stainless steel was subjected to severe shot peening: followed by plasma nitriding at 400 °C for 4 h. Characteristics of sample surface before and after treatment were analyzed by scanning electron microscopy, X-ray diffractometry and transmission electron microscopy techniques. Results showed that, this duplex treatment leads to formation of about 45 ?m thick nitride layer; without CrN precipitation. This is significantly high compared to reported data considering the temperature and duration of nitriding treatment employed. Selected area electron diffraction pattern from topmost surface confirmed the co-existence of austenite and martensite while subsurface layer was predominantly consisting of lath martensite. This indicates that major phase in the nitrided layer is martensitic in nature and nitrogen supersaturation leads to transformation of small fraction of martensite to expanded austenite. © 2016 Elsevier LtdItem Effect of shot peening coverage on surface nanostructuring of 316L stainless steel and its influence on low temperature plasma-nitriding(ASTM International, 2017) Jayalakshmi, M.; Badekai Ramachandra, B.; Bhat, K.U.Air-blast shot peening (ABSP) is a cost effective and industrially viable technique to produce nanostructured surface layer on metallic materials. In the present study, 316L stainless steel samples were subjected to shot peening at different peening coverage, from conventional to severe peening. Nanocrystalline structure was observed on the sample surface after peening and mechanical twins; intersection of multidirectional twins producing rhombic blocks were observed in the subsurface layer. Peening process led to the formation of strain induced martensite (?'), and its fraction was found to increase with the coverage. Depth of nanostructured layer and surface microhardness also increased with the increase in coverage, whereas surface roughness followed an opposite trend. Both peened and un-peened samples were subjected to plasma nitriding at 400°C for 4 h. Uniform and appreciably high case depth of about 45 ?m was observed in severely pre-peened (1000 % coverage) sample after nitriding treatment. No precipitation of CrN was observed. This highlights the marked influence of severe shot peening as a pre-treatment for low temperature plasma nitriding of austenitic stainless steels. © © 2017 by ASTM International.Item Metastable microstructures at the interface between AISI 321 steel and molten aluminum during hot-dip aluminizing(Elsevier B.V., 2018) Huilgol, P.; Udupa, K.R.; Bhat, K.U.The microstructure at the interface between AISI 321 stainless steel and molten aluminum was investigated which occurs during the process of hot-dip aluminizing. Microstructural characterization was carried out by scanning electron microscopy, transmission electron microscopy and X-ray diffraction. The study revealed the formation of metastable FeAlm and multiple twinned Al13Fe4 phases at the interface between steel and aluminum. Multiple twinned Al13Fe4 phase exhibits pseudo tenfold electron diffraction pattern. Another metastable phase Al3(NiFe) with an orthorhombic structure was formed as one of the eutectic phase mixture in the solidified aluminum topcoat. The Al3(NiFe) phase in the eutectic shares crystallographic orientation relationship with the Al matrix. Metastable intermetallic phases are being reported for the first time during hot-dip aluminizing. © 2018 Elsevier B.V.Item Microstructural investigations on the hot-dip aluminized AISI 321 stainless steel after diffusion treatment(Elsevier B.V., 2019) Huilgol, P.; Udupa, K.R.; Bhat, K.U.The microstructure of the hot-dip aluminized AISI 321 stainless steel was studied after diffusion treatment at 900 °C for 3 h. The microstructural characterization was carried out by scanning electron microscopy, transmission electron microscopy, and X-ray diffractometry. The microstructure of the as aluminized steel consisted of two regions, viz.; aluminum topcoat and aluminide layer. During the diffusion treatment, the coating transformed into a layered structure consisting of four layers. The Fe2Al5 phase was formed in the outermost layer and the presence of Al13Fe4 quasicrystalline approximant phase was observed. The innermost layer adjacent to the base metal transformed to ferrite phase with NiAl precipitates. Next, to this layer, a disordered FeAl phase was observed. The lattice parameter of the disordered FeAl phase was found to be larger than that of the ordered B2 FeAl phase. The layer between outer Fe2Al5 phase and disordered FeAl phase consists of a mixture of three phases, namely Fe2Al5, disordered FeAl and a new phase with the simple cubic structure. The phase with simple cubic structure shares cube on cube crystallographic orientation relationship with the disordered FeAl phase. © 2019 Elsevier B.V.