Faculty Publications
Permanent URI for this communityhttps://idr.nitk.ac.in/handle/123456789/18736
Publications by NITK Faculty
Browse
2 results
Search Results
Item Elevated temperature wear and friction performance of WC-CoCr/Mo and WC-Co/NiCr/Mo coated Ti-6Al-4V alloy(Elsevier Inc., 2024) Behera, N.; Ramesh, M.R.; Rahman, M.R.The effect of adding Mo to WC-based coatings on the microstructure and dry sliding wear performance at elevated temperatures is investigated. The WC-based coatings are deposited using a high-velocity oxy-fuel process on the titanium-31 substrate. The coating was characterized by microstructure, microhardness, porosity, surface roughness, density, and bond strength. The wear and friction behavior of coatings was evaluated using a ball-on disc tribometer at temperatures of 200, 400, 600, and 800 °C and loads of 20 and 30 N. SEM-EDS and an optical profilometer were utilized to evaluate the wear rate and mechanism. The microhardness and bond strength of WC-CoCr/10%Mo coating is more than that of WC-Co/20%NiCr/10%Mo coatings. The WC-CoCr, WC-CoCr/10%Mo, and WC-Co/20%NiCr/10%Mo coatings exhibited decreasing wear rates up to 600 °C, transitioning to an increase at 800 °C. The oxide phases of CoWO4 WO3 MoO3, CoMoO4, and NiMoO4, formed at 600 °C, aid in reducing the rate of wear and friction coefficient. However, the wear rate slightly increased at 800 °C due to vigorous oxidation and softness of coatings. The friction coefficient of WC-CoCr, WC-CoCr/10%Mo, and WC-Co/20%NiCr/10%Mo coating decreases with increasing temperatures due to the lubricating properties of oxide phases on the worn surface. The WC-CoCr/10%Mo coating demonstrates a lower friction and wear rate than the WC-CoCr and WC-Co/20%NiCr/10%Mo coating. At 200 °C, the predominant wear mechanisms were abrasive and fatigue wear, while at 800 °C, oxidative wear, abrasive wear, and adhesive wear were observed. © 2024Item Effect of molybdenum on high-temperature tribological performance in HVOF sprayed of WC-based coatings on superni-76(SAGE Publications Ltd, 2025) Behera, N.; Sarmah, P.; Chandramouli, T.V.; Ramesh, M.R.This study examines the effects of Mo on the high-temperature wear and friction behavior of HVOF-sprayed 70%WC-Co/25%Mo/5%C and 70%WC-CrC-Ni/30%Mo coatings on Superni-76. The ball-on-disc tribometer wear tests were conducted at different temperatures (300°C and 600°C) and loads (10 and 30?N) against counter body Al2O3 ball. Microstructures and phase formation were investigated using SEM/EDS and XRD. The characterization of coating microhardness, surface roughness, and coating density was examined. The 70%WC-Co/25%Mo/5%C coating showed lower surface roughness and higher microhardness values than the 70%WC-CrC-Ni/30%Mo coating. The wear rate of the substrate increases with an increase in temperature, whereas 70%WC-Co/25%Mo/5%C and 70%WC-CrC-Ni/30%Mo coatings decrease with temperature from 300°C to 600°C. The coefficient of friction of substrate and coating decreases with increasing temperatures. The worn surfaces of 70%WC-Co/25%Mo/5%C and 70%WC-CrC-Ni/30%Mo coating contain oxide phases (WO3, Cr2O5) and lubrication phases (M0.2W0.8O3, CoMoO4, and MoO3) at 600°C. These oxide phases reduced the coating wear rate and coefficient of friction at 600°C. The 70%WC-Co/25%Mo/5%C coating showed improved resistance to wear and lower friction coefficient than the substrate and 70%WC-CrC-Ni/30%Mo coating. At temperatures of 300°C, the main abrasive wear mechanism changes to oxidative wear when the temperature reaches 600°C for both coatings. © The Author(s) 2025.