Effect of equiaxed grains and secondary phase particles on mechanical properties and corrosion behaviour of CMT- based wire arc additive manufactured AZ31 Mg alloy
(Elsevier Ltd, 2023) Manjhi, S.K.; Sekar, P.; Bontha, S.; Balan, A.S.S.
Wire arc additive manufacturing (WAAM) has drawn tremendous attention for manufacturing large and complex components of lightweight material at a moderate cost due to its high deposition rate and energy efficiency. Generally, WAAM-Mg alloy comprises columnar and columnar dendrite grains due to high cooling rates and thermal gradients responsible for anisotropic mechanical properties. To overcome this challenge, in this work, CMT-WAAM, which generally uses comparatively low heat input (33% lower than conventional WAAM), was used to deposit AZ31 Mg thin wall. The metallurgical characterization of the deposited thin wall of the top (T), middle (M) and bottom (B) sections reveals equiaxed grains of average sizes ∼ 58, ∼ 63 and ∼ 38 µm, respectively. In addition, TEM results exhibit the formation of secondary phase particles, i.e., β-Mg17Al12 and ɳ-Al8Mn5. Further, the ultimate tensile strength (UTS) and % elongation (% EL) in the travel direction (UTS = 224 MPa, % EL= 23.47%) are superior to that obtained in the build direction (UTS = 217 MPa, % EL = 20.82%). The corrosion resistance of WAAMed AZ31 Mg alloy is higher than wrought (cold rolled) AZ31 Mg alloy in Hank's balanced salt solution (HBSS). The results of this study reveal the potential of CMT-WAAM to deposit different grades of Mg with desired microstructure, mechanical properties and corrosion resistance. © 2023 CIRP
Hybrid additive manufacturing of ER70S6 steel and Inconel 625: A study on microstructure and mechanical properties
(Elsevier Ltd, 2023) Rodrigues, J.P.; Thanumoorthy, R.S.; Manjhi, S.K.; Sekar, P.; Arumuga Perumal, D.A.; Bontha, S.; Balan, A.S.S.
Hybrid Additive Manufacturing (HAM) is currently being explored because of its potential to achieve trade-off between build capacity and feature resolution. The present study aims at fabricating ER70S6-Inconel 625 (IN625) bimetallic clad using hybrid Wire Arc Additive Manufacturing (WAAM) and Laser Directed Energy Deposition (LDED) processes. Microstructure evaluation was performed at the cross section of bimetallic clad for distinct materials as well as the interface. WAAM built ER70S6 revealed equiaxed ferritic grains, whereas laser deposited IN625 region showed columnar dendrites with under developed secondary arms. However, the first layer of IN625 exhibited columnar dendrite with secondary arms due to the influence of diffused Fe from the base ER70S6 steel under the action of concentrated laser heat source, which was revealed by energy dispersive spectroscopy (EDS) maps. The measured microhardness across the cross section of the deposit showed values corresponding to inherent material system. The interface did not reveal presence of any intermetallic phases which was confirmed by hardness results and X-Ray diffraction. Shear test revealed superior bond strength between the two materials, maintaining average strength of 452 MPa. The fractography images exhibited fine dimples along with cleavages indicating mixed fracture characteristics. This additive manufacturing method explores a new dimension in multi-material fabrication which, when customized for different materials, serve critical areas in the aerospace and defence sector. © 2023 Elsevier Ltd
Effect of burnishing strategies on surface integrity, microstructure and corrosion performance of wire arc additively manufactured AZ31 Mg alloy
(KeAi Publishing Communications Ltd., 2025) Manjhi, S.K.; R, O.; Bontha, S.; Balan, A.S.S.
AZ31 Mg alloy is an emerging material that has received considerable attention in aerospace, automotive, and temporary biodegradable implant applications owing to its attractive properties, such as low density, high specific strength, and biodegradability. Nevertheless, some shortcomings in Mg alloys are their low ductility, which is associated with challenging its manufacturing, and poor corrosion resistance associated with unreliable components. Therefore, a cold metal transfer wire arc additive manufacturing (CMT-WAAM) process is used to manufacture AZ31 Mg alloy and achieved 29.4 % ductility by controlling the gas porosity, keyhole porosity, and internal cracks. Further, severe plastic deformation is induced on the surface of deposited parts by low plasticity burnishing (LPB) with parallel and cross-pattern burnishing to modulate their surface to slow down the kinetics of the corrosion damage. The average surface roughness (Sa) of the cross-burnishing pattern is 0.235 ?m, which is 123.6 % lower than the parallel burnished and 261.7 % lower than the milled specimens. The residual stress (RS) of WAAM is 40 MPa with a tensile nature; however, it is drastically reduced and develops compressive RS of 45 MPa under a parallel burnishing pattern and 62 MPa under a cross-burnishing pattern. Moreover, LPB with cross pattern deformed ?395 ?m depth of WAAMed AZ31 workpiece, which is ?45 % higher than deformed depth (?272 ?m) by parallel pattern burnishing. The electrochemical corrosion rate of the WAAM specimen is 9.71 mm/year, and it is reduced to 1.82 mm/year under LPB caused by compressive residual stress and grain refinement. © 2024 The Authors