Faculty Publications
Permanent URI for this communityhttps://idr.nitk.ac.in/handle/123456789/18736
Publications by NITK Faculty
Browse
5 results
Search Results
Item Studies on concrete cylinders subjected to elevated temperatures(2010) Babu Narayan, K.S.; Anil Kumar, G.; Chandrakala, C.; Shashikumar, H.M.; Venkataramana, K.; Yaragal, S.C.; Chinnagiri Gowda, H.C.; Reddy, G.R.; Sharma, A.Concrete is a poor conductor of heat, but can suffer considerable damage when exposed to fire. Concrete in structures is likely to be exposed to high temperatures during fire. The relative properties of concrete after such an exposure are of great importance in terms of the serviceability of buildings. Unraveling the heating history of concrete is important to forensic research or to determine whether a fire exposed concrete structures and its components are still structurally sound or not. Assessment of fire damage concrete structures usually starts with visual observation of color change, cracking and spalling. On heating, a change in color from normal to pink is often observed and this is useful since it coincides with the onset of significant loss of concrete strength. This work reports the characteristics of concrete at elevated temperatures. Popular normal strength grades (M20, M25, M30, M35, M40 and M45) produced by Ready Mix Concrete (RMC) India, Mangalore have been used in production of test specimens (150 mm diameter and 300mm height cylinders) to obtain more meaningful and realistic data. In the preliminary phase 150 mm diameter and 300mm height cylinders were cast, cured and tested by destructive method for gathering data on strength characteristics. Later these test samples were subjected to elevated temperatures ranging from 100°C to 800°C, in steps of 100°C with a retention period of 2 hours. After exposure, weight losses were determined and then again destructive tests were conducted to estimate the residual split tensile strength. Test results indicated that weight and strength significantly reduces with an increase in temperature. © 2010 CAFET-INNOVA TECHNICAL SOCIETY. All rights reserved.Item Strength retention characteristics of concrete cubes subjected to elevated temperatures(2010) Yaragal, S.C.; Clarke, K.S.; Mahesh Babu, K.; Ashokumar, S.; Venkataramana, K.; Babu Narayan, K.S.; Chinnagiri Gowda, H.C.; Reddy, G.R.; Sharma, A.Concrete in structures is likely to be exposed to high temperatures during fire. The relative properties of concrete after such an exposure are of great importance in terms of the serviceability of buildings. The probability of its exposure to elevated temperatures is high due to natural hazards, accidents and sabotages. Therefore, the performance of concrete during and after exposure to elevated temperature is a subject of great interest to the designer. Physical changes like cracking, colour change, spalling and chemical changes like decomposition of Ca(OH)2 and the C-S-H gel take place when subjected to elevated temperatures. This work reports the characteristics of concrete at elevated temperatures. Popular normal strength grades (M20, M25, M30, M35, M40 and M45) produced by Ready Mix Concrete (RMC) India, Mangalore have been used in production of test specimens (150 mm cubes) to obtain more meaningful and realistic data. In the preliminary phase 150 mm cubes were cast, cured and tested by destructive method for gathering data on strength characteristics. Later these test samples were subjected to elevated temperatures ranging from 100°C to 800°C, in steps of 100°C with a retention period of 2 hours. After exposure, weight losses were determined and then again destructive tests were conducted to estimate the residual compressive strength. Test results indicated that weight and strength significantly reduces with an increase in temperature. © 2010 CAFET-INNOVA TECHNICAL SOCIETY.Item Studies on normal strength concrete cubes subjected to elevated temperatures(2010) Yaragal, S.C.; Babu Narayan, K.S.; Venkataramana, K.; Kulkarni, K.S.; Gowda, H.C.C.; Reddy, G.R.; Sharma, A.Concrete in structures is likely to be exposed to high temperatures during fire. The probability of its exposure to elevated temperatures is high due to natural hazards, accidents and sabotages. Therefore, the performance of concrete during and after exposure to elevated temperature is a subject of great importance and interest to the designer. Popular normal strength grades of concrete produced by Ready Mix Concrete (RMC) India, Mangalore have been used in production of test specimens (150 mm cubes), cured and tested by destructive method for gathering data on strength characteristics. Later, these test samples were subjected to elevated temperatures ranging from 100 C to 800 C, in steps of 100 C with a retention period of 2 hours. After exposure, weight losses and the residual compressive strength retention characteristics are studied. Test results indicated that weight and strength significantly reduces with an increase in temperature. Residual compressive strength prediction equations are proposed for normal strength concretes subjected to elevated temperatures.Item Strength characteristics of concrete exposed to elevated temperatures and cooled under different regimes(2012) Yaragal, S.C.; Babu Narayan, K.S.; Adari, S.Concrete loses strength in the event of accidental fires. The residual strength of normal strength concrete is of vital importance for ascertaining serviceability of buildings after the event of fires. Strength loss in concrete is dependent on the temperature of exposure, its duration and the way it gets cooled. In this study concrete cubes of size 100 mm have been cast for M25 grade of concrete, 28 days water cured. The specimens were subjected to elevated temperatures of 150°C, 250°C, 350°C, 450°C and 550°C with a retention period of 1 hour. After 1 hour of exposure, specimens were allowed to cool under different cooling regimes to ambient temperature. Later their appearance, colour and cracks were observed and also weight losses were determined. Further, destructive tests were conducted to estimate residual compressive and split tensile strengths. Important performance changes have been presented and discussed. Split tensile strengths are related to compressive strengths for all the cases of cooling regimes.Item Assessment of thermally deteriorated concrete by drilling resistance test and sound level(Maik Nauka Publishing / Springer SBM compmg@maik.ru, 2017) Kulkarni, K.S.; Yaragal, S.C.; Babu Narayan, K.S.; Vardhan, H.Concrete being the most versatile and widely used construction material finds application in varied range of structures. Many of these like chimneys, furnaces and reactors have to sustain high temperatures and perhaps all structures have to perform at elevated temperatures in the event of fire accidents. Concrete at elevated temperatures undergoes changes in its physical structure and chemical composition and loses its strength characteristics. Need for quick assessment of fire damaged concrete for strength characteristics, has motivated this work, which explores the potential of drilling resistance test on concrete as a Non Destructive Testing (NDT) tool. Drilling times, penetration depths and sound level measurement while drilling have been recorded and analysed to provide monograms that are handy as reckoners in failure forensics. © 2017, Pleiades Publishing, Ltd.