Faculty Publications
Permanent URI for this communityhttps://idr.nitk.ac.in/handle/123456789/18736
Publications by NITK Faculty
Browse
8 results
Search Results
Item Hot corrosion resistance of air plasma sprayed ceramic Sm2SrAl2O7 (SSA) thermal barrier coatings in simulated gas turbine environments(Elsevier Ltd, 2018) Baskaran, T.; Arya, S.Samarium strontium aluminate (Sm2SrAl2O7-SSA) and Yttria-stabilized zirconia (YSZ) thermal barrier coatings (TBCs) were developed on NiCrAlY bond coated Inconel 718 superalloy substrate using air plasma spray process. The hot corrosion study was conducted in simulated gas turbine environments (molten mixtures of 50 wt% Na2SO4 + 50 wt% V2O5 and 90 wt% Na2SO4 + 5 wt% V2O5 + 5 wt% NaCl) for two different temperatures of 700 and 900 °C. A developed SSA TBCs showed about 8% and 22% lower lifetime at 700 and 900 °C, respectively than YSZ TBCs in 50 wt% Na2SO4 + 50 wt% V2O5 (vanadate). The hot corrosion life of SSA TBCs being found about 13% and 39% lower than YSZ TBCs in 90 wt% Na2SO4 + 5 wt% V2O5 + 5 wt% NaCl (chloride) at 700 and 900 °C, respectively. X-ray diffraction results showed the formation of SmVO4, SrV2O6, and SrSO4 as a major hot corrosion product in 50 wt% Na2SO4 + 50 wt% V2O5 and 90 wt% Na2SO4 + 5 wt% V2O5 + 5 wt% NaCl environments respectively for SSA TBCs. Similarly, YSZ TBCs also showed YVO4 as hot corrosion product in vanadate and chloride environments. Both the TBCs suffer a more severe hot corrosion attack in chloride environment at 900 °C. The leaching of Sr2+ and Y3+ ions from SSA and YSZ respectively play a vital role in the destabilization of coating in vanadate and chloride environments at 700 and 900 °C. In both SSA and YSZ TBCs, the leaching of ion has significantly low influence as compared to attack by chloride ions at the bond coat-top coat interface in the presence of chloride environment. The hot corrosion resistance of SSA TBCs was improved three times higher in the presence of MgO and NiO inhibitor in vanadate environment at 900 °C mainly due to the formation of a stable Ni3V2O8 phase at the surface. © 2018 Elsevier Ltd and Techna Group S.r.l.Item Effect of zinc and rare-earth element addition on mechanical, corrosion, and biological properties of magnesium(Cambridge University Press, 2018) Kottuparambil, R.R.; Bontha, S.; Ramesh, M.R.; Arya, S.; Jana, A.; Das, M.; Balla, V.K.; Amrithalingam, S.; Prabhu, T.R.The present work aims to understand the effect of zinc and rare-earth element addition (i.e., 2 wt% Gd, 2 wt% Dy, and 2 wt% of Gd and Nd individually) on the microstructure evolution, mechanical properties, in vitro corrosion behavior, and cytotoxicity of Mg for biomedical application. The microstructure results indicate that the Mg-Zn-Gd alloy consists of the lamellar long period stacking ordered phase. The electrochemical and immersion corrosion behavior were studied in Hanks balanced salt solution. Enhanced corrosion resistance with reduced hydrogen evolution volume and magnesium (Mg2+) ion release were estimated for the Mg-Zn-Gd alloy as compared to the other two alloy systems. At the early stage of corrosion, formation of the oxide film inhibited the corrosion propagation. However, at the later stages, the breaking of the oxide film leads to shallow pitting mode of corrosion. The ultimate tensile strength of Mg-Zn-Gd-Nd is better than the other two alloys due to the uniform distribution of the Mg12Nd precipitate phase. The moderate strength in the Mg-Zn-Gd alloy is due to the low volume fraction of the secondary phase. The MTT (methylthiazoldiphenyl-tetrazolium bromide) assay study was carried out to understand the cell cytotoxicity on the alloy surfaces. Studies revealed that all three alloys had significant cellular adherence and no adverse effect on cells. © 2018 Materials Research Society.Item On the corrosion resistance of some selective laser melted alloys(Elsevier B.V., 2018) Suryawanshi, J.; Baskaran, T.; Prakash, O.; Arya, S.; Ramamurty, U.The electrochemical corrosion resistances of selective laser melted (SLM) 316 L austenitic stainless steel (SS), 18(Ni) 300-grade maraging steel (MS), and Al-12 wt.% Si (AS) alloy in a 0.1 M NaCl solution at room temperature were evaluated. The effects of laser scanning strategy (single melt vs. checker board styles), post-SLM heat treatment, and corroding surface orientation (with respect to the scan and build directions) on the corrosion behavior were examined. In all cases, results were compared with those obtained on samples with the same compositions, but manufactured using conventional means. The experimental results show that, for the particular set of experimental conditions employed in this study, SLM in general improves the corrosion resistances of Al-12 wt.% Si and stainless steel alloys and degrades the corrosion resistance of the maraging steel, in comparison to the respective corrosion resistances of their conventionally manufactured counterparts. These results are discussed in terms of microstructural refinement and porosity that are common to the SLM alloys. © 2018 Acta Materialia Inc.Item Laser surface modification of Mg-Zn-Gd alloy: Microstructural, wettability and in vitro degradation aspects(Institute of Physics Publishing helen.craven@iop.org, 2018) Rakesh, K.R.; Bontha, S.; Ramesh, M.R.; Arya, S.; Das, M.; Balla, V.K.; Srinivasan, A.Mg-Zn-Gd have great potential for biomedical applications owing to excellent bioactivity and non-toxicity properties. In the present study, laser surface melting (LSM) was carried out on newly developed Mg-1Zn -2Gd (wt%) alloy. Effects of laser energy on microstructural evolution, corrosion properties, surface energy, and hardness have been investigated. The surface modified sample processed at different energy densities showed fine grain structure in the melt zone compared to the untreated substrate. Grain refinement in the laser melted region improved the hardness by 60%. The surface roughness was found to be increased with increasing laser energy density. At higher energy density, removal of materials from the surface is enhanced, resulting in deeper grooves and higher surface roughness. The wettability studies indicated that the variations in surface geometry, grain size and surface roughness of LSM samples strongly influence the surface energy and hydrophilicity. Improved wetting of LSM sample was achieved owing to grain refinement and low surface roughness. The corrosion resistance determined by immersion and electrochemical methods of laser melted sample in Hank's balanced salt solution improved considerably due to grain refinement, meltpool depth and uniform distribution of secondary phases. © 2018 IOP Publishing Ltd.Item Effects of combined multiaxial forging and rolling process on microstructure, mechanical properties and corrosion behavior of a Cu-Ti alloys(Institute of Physics Publishing helen.craven@iop.org, 2019) Ramesh, S.; Anne, G.; Shivananda Nayaka, H.; Sahu, S.; Arya, S.Combined multiaxial forging (MAF) and rolling was performed on Cu-3% Ti (wt%) alloy at room temperature with emphasis on microstructural evolution, improvement in mechanical properties, and corrosion resistance. Microstructural changes were confirmed from various characterization techniques, and co-related with mechanical properties. TEM analysis revealed high shear band density in the 3 pass MAF + 90% rolled sample appearing due to high strain. EBSD analysis revealed transformation to low angle grain boundaries from high angle grain boundaries. Maximum microhardness and UTS reached to 340 HV and 960 MPa, respectively in the processed samples. Significant grain refinement was observed in MAF processed Cu-3%Ti alloy, and after combined MAF + rolling, higher dislocation density and refinement of shear bands were observed. In addition, potentio-dynamic polarization test was used to study the corrosion behavior of the alloy. Scanning electron microscope (SEM) was used to analyze the corroded surface morphology. © 2019 IOP Publishing Ltd.Item Optimization of ball-burnishing process parameters on surface roughness, micro hardness of Mg-Zn-Ca alloy and investigation of corrosion behavior(Institute of Physics Publishing helen.craven@iop.org, 2019) Ramesh, S.; Aditya Kudva, S.; Anne, G.; Manne, B.; Arya, S.In this work, optimization of ball burnishing parameters (depth of press, feed, burnishing force, number of passes) and their effect on surface roughness, microhardness and corrosion behavior of Mg-4%Zn-1%Ca alloy is investigated. The Taguchi optimization technique was used to determine the number of experiments and by considering S/N ratios, right combination of ball burnishing parameters were selected. Results obtained from the experiments were investigated and it is understood that depth of press, feed and number of passes have a significant effect on surface roughness, microhardness and consequently improves corrosion resistance of Mg-4%Zn-1%Ca alloy. From ball burnishing experiments it is deduced that there is large increase in microhardness of 107 Hv and surface roughness of 129 nm, achieved for the depth of press 0.45 mm, burnishing force 250 N, feed 450 mm min-1 and number of passes: 2. Corrosion behavior of the alloys were analyzed using potentiodynamic polarization and electrochemical impedance spectroscopy techniques in Hank's balanced salt solution. The lowest corrosion rate was observed in DFN 442 sample (1.43 mm y-1) which is 4.7 times better than the homogenized alloy (6.73 mm y-1). It has been found that the ball burnishing plays an important role on surface roughness, microhardness and corrosion behavior of Mg-4%Zn-1%Ca alloy. © 2019 IOP Publishing Ltd.Item Influence of Multiaxial Cryoforging on Microstructural, Mechanical, and Corrosion Properties of Copper-Titanium Alloy(Springer, 2019) Ramesh, S.; Shivananda Nayaka, H.S.; Sahu, S.; Gopi, K.R.; Shivaram, M.J.; Arya, S.Multiaxial forging (MAF) was used to process Cu-4.5%Ti (wt.%) alloy at cryogenic temperature up to three cycles with a cumulative strain of 1.64. Microstructures, mechanical, and corrosion properties of as-received and deformed samples were analyzed. Microstructural analysis showed that average grain size decreased from 70 µm to 200 nm, and electron backscattered diffraction (EBSD) analysis revealed the transformation of high-angle grain boundaries (HAGBs) to low-angle grain boundaries (LAGBs). Variations in intensity of peaks were observed by x-ray diffraction (XRD) technique. Microstructural investigation showed elongated grains with shear bands having width ~ 200 nm for 3-cycle sample. Tensile testing and micro-hardness tests showed improvements in ultimate tensile strength (UTS), yield strength (YS), and micro-hardness, with the increase in MAF cycles. Ultimate tensile strength and hardness increased from 605 MPa and 252 HV (for as-received) to 1284 MPa and 428 HV for three cycles of MAF-processed sample, respectively. Improvement in strength and hardness was attributed to refined grain structure. Corrosion study was carried out for different cycles of MAF-processed samples using potentiodynamic polarization, and corroded surfaces were analyzed using scanning electron microscopy (SEM) and energy-dispersive spectroscopy (EDS) analysis. © 2019, ASM International.Item Surface modification of multi-directional forged biodegradable Mg-Zn alloy by ball burnishing process: Modeling and analysis using deep neural network(Elsevier Ltd, 2021) Ramesh, S.; Anne, G.; Bhat, N.; Aithal, G.; Shivananda Nayaka, H.; Arya, S.This research investigates the feasibility of improving surface integrity of the Mg-2%Zn alloy via a novel combined process of multidirectional forging (MDF) with ball burnishing technique. Mg-2%Zn alloy was subjected to multidirectional forging up to 5 passes at 280 °C and same sample is ball burnished with depth of press of 0.3 mm, feed of 300 mm/min and force of 250 N for 1 pass. Microstructure (optical and transmission electron microscope), phases (X ray diffraction), roughness (atomic force microscope) and mechanical properties (microhardness and tensile) were analyzed for cast, MDF processed and MDF + ball burnished samples. The study also defines a new reliability simulation framework to predict the roughness and hardness of the MDF + ball burnished samples using Deep Neural Network (DNN) approach. For the analysis, depth of press, feed and number of passes served as inputs for the DNN model. After configuring and training procedure of the model, the predicted roughness and microhardness of the MDF + ball burnished were compared with the results of experimental data. A large increase of microhardness was observed for MDF-5 + BB-1 (5 pass MDF processed Mg-2%Zn alloy + Ball burnished sample), found to be 98 Hv and surface roughness of 306 nm was achieved. According to the results, the obtained R-squared value is very close to the 99.5 percentage from the model for predicting roughness and hardness which is a promising result. Corrosion behavior of the AS-1, MDF-5 and MDF-5 + BB-1 was evaluated in Hank's balanced salt solution. Corrosion rate of the MDF-5 + BB-1 samples were found to be 0.87 mm/y which is 7 times better than that of AS-1 samples (6.10 mm/y). Grain refinement and residual stresses were higher in the MDF-5 + BB-1 sample, which helped significantly to enhance corrosion resistance. © 2021 The Society of Manufacturing Engineers