Faculty Publications
Permanent URI for this communityhttps://idr.nitk.ac.in/handle/123456789/18736
Publications by NITK Faculty
Browse
4 results
Search Results
Item Effect of zinc and rare-earth element addition on mechanical, corrosion, and biological properties of magnesium(Cambridge University Press, 2018) Kottuparambil, R.R.; Bontha, S.; Ramesh, M.R.; Arya, S.; Jana, A.; Das, M.; Balla, V.K.; Amrithalingam, S.; Prabhu, T.R.The present work aims to understand the effect of zinc and rare-earth element addition (i.e., 2 wt% Gd, 2 wt% Dy, and 2 wt% of Gd and Nd individually) on the microstructure evolution, mechanical properties, in vitro corrosion behavior, and cytotoxicity of Mg for biomedical application. The microstructure results indicate that the Mg-Zn-Gd alloy consists of the lamellar long period stacking ordered phase. The electrochemical and immersion corrosion behavior were studied in Hanks balanced salt solution. Enhanced corrosion resistance with reduced hydrogen evolution volume and magnesium (Mg2+) ion release were estimated for the Mg-Zn-Gd alloy as compared to the other two alloy systems. At the early stage of corrosion, formation of the oxide film inhibited the corrosion propagation. However, at the later stages, the breaking of the oxide film leads to shallow pitting mode of corrosion. The ultimate tensile strength of Mg-Zn-Gd-Nd is better than the other two alloys due to the uniform distribution of the Mg12Nd precipitate phase. The moderate strength in the Mg-Zn-Gd alloy is due to the low volume fraction of the secondary phase. The MTT (methylthiazoldiphenyl-tetrazolium bromide) assay study was carried out to understand the cell cytotoxicity on the alloy surfaces. Studies revealed that all three alloys had significant cellular adherence and no adverse effect on cells. © 2018 Materials Research Society.Item On the corrosion resistance of some selective laser melted alloys(Elsevier B.V., 2018) Suryawanshi, J.; Baskaran, T.; Prakash, O.; Arya, S.; Ramamurty, U.The electrochemical corrosion resistances of selective laser melted (SLM) 316 L austenitic stainless steel (SS), 18(Ni) 300-grade maraging steel (MS), and Al-12 wt.% Si (AS) alloy in a 0.1 M NaCl solution at room temperature were evaluated. The effects of laser scanning strategy (single melt vs. checker board styles), post-SLM heat treatment, and corroding surface orientation (with respect to the scan and build directions) on the corrosion behavior were examined. In all cases, results were compared with those obtained on samples with the same compositions, but manufactured using conventional means. The experimental results show that, for the particular set of experimental conditions employed in this study, SLM in general improves the corrosion resistances of Al-12 wt.% Si and stainless steel alloys and degrades the corrosion resistance of the maraging steel, in comparison to the respective corrosion resistances of their conventionally manufactured counterparts. These results are discussed in terms of microstructural refinement and porosity that are common to the SLM alloys. © 2018 Acta Materialia Inc.Item Effects of combined multiaxial forging and rolling process on microstructure, mechanical properties and corrosion behavior of a Cu-Ti alloys(Institute of Physics Publishing helen.craven@iop.org, 2019) Ramesh, S.; Anne, G.; Shivananda Nayaka, H.; Sahu, S.; Arya, S.Combined multiaxial forging (MAF) and rolling was performed on Cu-3% Ti (wt%) alloy at room temperature with emphasis on microstructural evolution, improvement in mechanical properties, and corrosion resistance. Microstructural changes were confirmed from various characterization techniques, and co-related with mechanical properties. TEM analysis revealed high shear band density in the 3 pass MAF + 90% rolled sample appearing due to high strain. EBSD analysis revealed transformation to low angle grain boundaries from high angle grain boundaries. Maximum microhardness and UTS reached to 340 HV and 960 MPa, respectively in the processed samples. Significant grain refinement was observed in MAF processed Cu-3%Ti alloy, and after combined MAF + rolling, higher dislocation density and refinement of shear bands were observed. In addition, potentio-dynamic polarization test was used to study the corrosion behavior of the alloy. Scanning electron microscope (SEM) was used to analyze the corroded surface morphology. © 2019 IOP Publishing Ltd.Item Optimization of ball-burnishing process parameters on surface roughness, micro hardness of Mg-Zn-Ca alloy and investigation of corrosion behavior(Institute of Physics Publishing helen.craven@iop.org, 2019) Ramesh, S.; Aditya Kudva, S.; Anne, G.; Manne, B.; Arya, S.In this work, optimization of ball burnishing parameters (depth of press, feed, burnishing force, number of passes) and their effect on surface roughness, microhardness and corrosion behavior of Mg-4%Zn-1%Ca alloy is investigated. The Taguchi optimization technique was used to determine the number of experiments and by considering S/N ratios, right combination of ball burnishing parameters were selected. Results obtained from the experiments were investigated and it is understood that depth of press, feed and number of passes have a significant effect on surface roughness, microhardness and consequently improves corrosion resistance of Mg-4%Zn-1%Ca alloy. From ball burnishing experiments it is deduced that there is large increase in microhardness of 107 Hv and surface roughness of 129 nm, achieved for the depth of press 0.45 mm, burnishing force 250 N, feed 450 mm min-1 and number of passes: 2. Corrosion behavior of the alloys were analyzed using potentiodynamic polarization and electrochemical impedance spectroscopy techniques in Hank's balanced salt solution. The lowest corrosion rate was observed in DFN 442 sample (1.43 mm y-1) which is 4.7 times better than the homogenized alloy (6.73 mm y-1). It has been found that the ball burnishing plays an important role on surface roughness, microhardness and corrosion behavior of Mg-4%Zn-1%Ca alloy. © 2019 IOP Publishing Ltd.