Faculty Publications
Permanent URI for this communityhttps://idr.nitk.ac.in/handle/123456789/18736
Publications by NITK Faculty
Browse
11 results
Search Results
Item Microstructure Evolution and Mechanical and Corrosion Behavior of Accumulative Roll Bonded Mg-2%Zn/Al-7075 Multilayered Composite(Springer New York LLC barbara.b.bertram@gsk.com, 2017) Anne, G.; Ramesh, M.R.; Shivananda Nayaka, H.; Arya, S.B.; Sahu, S.Multilayered composite of Mg-2%Zn/Al-7075 was developed by accumulative roll bonding (ARB) of wrought Mg-2%Zn and aluminum 7075 alloy. The Mg-2%Zn/Al-7075 multilayered composite exhibited density of 2295 kg/m3 and an average grain size of 1 and 1.3 ?m in Mg-2%Zn and Al-7075 layers, respectively. A thorough microstructural characterization was performed on the composites by scanning electron microscope, electron backscatter diffraction (EBSD), transmission electron microscope and phase analysis by x-ray diffraction. In addition, mechanical properties were evaluated by microhardness and tensile tests. Corrosion behavior of the multilayered composite was examined using electrochemical polarization test. EBSD analysis showed the presence of ultrafine grains with high-angle grain boundaries. The composite exhibited a significant improvement in ultimate tensile strength (~1.82 times) and elongation (~1.5 times) as compared with Mg-2%Zn alloy, after four-pass ARB process. © 2017, ASM International.Item Effects of combined multiaxial forging and rolling process on microstructure, mechanical properties and corrosion behavior of a Cu-Ti alloys(Institute of Physics Publishing helen.craven@iop.org, 2019) Ramesh, S.; Anne, G.; Shivananda Nayaka, H.; Sahu, S.; Arya, S.Combined multiaxial forging (MAF) and rolling was performed on Cu-3% Ti (wt%) alloy at room temperature with emphasis on microstructural evolution, improvement in mechanical properties, and corrosion resistance. Microstructural changes were confirmed from various characterization techniques, and co-related with mechanical properties. TEM analysis revealed high shear band density in the 3 pass MAF + 90% rolled sample appearing due to high strain. EBSD analysis revealed transformation to low angle grain boundaries from high angle grain boundaries. Maximum microhardness and UTS reached to 340 HV and 960 MPa, respectively in the processed samples. Significant grain refinement was observed in MAF processed Cu-3%Ti alloy, and after combined MAF + rolling, higher dislocation density and refinement of shear bands were observed. In addition, potentio-dynamic polarization test was used to study the corrosion behavior of the alloy. Scanning electron microscope (SEM) was used to analyze the corroded surface morphology. © 2019 IOP Publishing Ltd.Item Influence of Multidirectional Forging on Microstructural, Mechanical, and Corrosion Behavior of Mg-Zn Alloy(Springer New York LLC barbara.b.bertram@gsk.com, 2019) Ramesh, S.; Anne, G.; Shivananda Nayaka, H.S.; Sahu, S.; Ramesh, M.R.Multidirectional forging (MDF) was applied to Mg-6%Zn alloy up to 5 passes successfully at 280 °C. MDF-processed materials were characterized using optical microscope, scanning electron microscope, electron backscatter diffraction, transmission electron microscope, and x-ray diffraction. Obtained results showed a significant reduction in grain size (up to 3.8 ?m) having a large fraction of high-angle grain boundaries after 5 passes of MDF process. Maximum tensile strength of 230 MPa was achieved for 5-pass MDF-processed Mg-6%Zn alloy which is about ~ 2.0 times higher in comparison with that of homogenized alloy (117 MPa) and was attributed to higher dislocations density and grain refinement. Corrosion behavior of the alloy was investigated in 0.1 M NaCl solution using potentiodynamic polarization test, electrochemical impedance spectra analysis, and immersion tests. It was found that the corrosion rate of 5-pass MDF sample improved (0.34 mm/year) ~2.5 times in comparison with that of homogenized Mg-6%Zn alloy (0.86 mm/year) due to fine grain structure, which creates more grain boundaries that act as a corrosion barrier. © 2019, ASM International.Item Optimization of ball-burnishing process parameters on surface roughness, micro hardness of Mg-Zn-Ca alloy and investigation of corrosion behavior(Institute of Physics Publishing helen.craven@iop.org, 2019) Ramesh, S.; Aditya Kudva, S.; Anne, G.; Manne, B.; Arya, S.In this work, optimization of ball burnishing parameters (depth of press, feed, burnishing force, number of passes) and their effect on surface roughness, microhardness and corrosion behavior of Mg-4%Zn-1%Ca alloy is investigated. The Taguchi optimization technique was used to determine the number of experiments and by considering S/N ratios, right combination of ball burnishing parameters were selected. Results obtained from the experiments were investigated and it is understood that depth of press, feed and number of passes have a significant effect on surface roughness, microhardness and consequently improves corrosion resistance of Mg-4%Zn-1%Ca alloy. From ball burnishing experiments it is deduced that there is large increase in microhardness of 107 Hv and surface roughness of 129 nm, achieved for the depth of press 0.45 mm, burnishing force 250 N, feed 450 mm min-1 and number of passes: 2. Corrosion behavior of the alloys were analyzed using potentiodynamic polarization and electrochemical impedance spectroscopy techniques in Hank's balanced salt solution. The lowest corrosion rate was observed in DFN 442 sample (1.43 mm y-1) which is 4.7 times better than the homogenized alloy (6.73 mm y-1). It has been found that the ball burnishing plays an important role on surface roughness, microhardness and corrosion behavior of Mg-4%Zn-1%Ca alloy. © 2019 IOP Publishing Ltd.Item Influence of Ball Burnishing Process on Equal Channel Angular Pressed Mg-Zn-Si Alloy on the Evolution of Microstructure and Corrosion Properties(Springer Science and Business Media B.V., 2021) Ramesh, S.; Anne, G.; Kumar, G.; Jagadeesh, C.; Shivananda Nayaka, H.In the present study, Mg-4Zn-1Si alloy was subjected to equal channel angular pressing (ECAP) up to 4 passes at 300 °C, followed by ball burnishing using 0.3 mm depth of press, 300 mm/min feed and 1 pass successfully. The effect of ECAP and ECAP + ball burnishing process on microstructure, mechanical properties (tensile and hardness) and corrosion behavior was systematically investigated. After 4 pass ECAP, initial coarse grains (210 ?m) were refined and average grain size is 6 ?m and after ball burnishing, the grain size is found to be 3.3 ?m. Microstructure evolution is discussed using optical images, scanning electron microscope images and transmission electron microscope images. For ECAP samples, maximum strength and hardness was recorded at 3 pass. Both strength and hardness decreased for 4 pass ECAP processed samples, even though grain size decreased, this is because of texture modification in the material. ECAP 4 pass + ball burnished samples exhibited 48.5% enhancement of microhardness as compared to 4 pass ECAP samples. Corrosion resistance of the samples decreased with increase in the number of ECAP passes, this is due to strain-induced grain refinement with more crystalline defects in samples. Combined process of ECAP and ball burnishing effectively reduces the Icorr and this consequently reduces corrosion rate of the Mg–4Zn-1Si alloy. © 2020, Springer Nature B.V.Item Effect of Equal Channel Angular Pressing on Properties Evaluation of Biodegradable Mg-Zn-Mn Alloy(Springer Science and Business Media Deutschland GmbH, 2021) Ramesh, S.; Kumar, G.; Jagadeesh, C.; Anne, G.; Shivananda Nayaka, H.Equal channel angular pressing (ECAP) was used to process Mg-4Zn-1Mn alloy at 300 °C using route Bc up to 4 pass with a cumulative strain of 3.2. Optical microscope (OM), microstructures results shows homogenized sample grain size was 260 µm, after 4 pass ECAP grain size was decreased to 6 µm. Electron back-scattered diffraction (EBSD) shows the misorientation angle converted from low-angle grain boundaries (LAGB) to high-angle grain boundaries (HAGB). Dislocation density and fine grains were observed from transmission electron microscope (TEM) images. Strength has been increased from 156 to 218 MPa and hardness increased to 68 Hv after 4 pass of ECAP. Fractography analysis revealed that dimple size decreases as ECAP passes increased. XRD analysis shows the peak broadening and intensity variation, because of grain refinement. The corrosion behavior of the homogenized and ECAP-processed samples were investigated by electrochemical tests using simulated body fluids (SBF) at 37 ± 1 °C. The lower corrosion resistance of ECAP-processed Mg-4Zn-1Mn alloy attributed to the strain-induced crystalline defects, subgrain boundaries and high-density dislocations. Enhanced strength and ductility combined with lower corrosion resistance of ECAP-processed Mg-4Zn-1Mn has greater potentials for biomedical implants. © 2021, The Author(s), under exclusive licence to Springer Nature Switzerland AG.Item Surface modification of multi-directional forged biodegradable Mg-Zn alloy by ball burnishing process: Modeling and analysis using deep neural network(Elsevier Ltd, 2021) Ramesh, S.; Anne, G.; Bhat, N.; Aithal, G.; Shivananda Nayaka, H.; Arya, S.This research investigates the feasibility of improving surface integrity of the Mg-2%Zn alloy via a novel combined process of multidirectional forging (MDF) with ball burnishing technique. Mg-2%Zn alloy was subjected to multidirectional forging up to 5 passes at 280 °C and same sample is ball burnished with depth of press of 0.3 mm, feed of 300 mm/min and force of 250 N for 1 pass. Microstructure (optical and transmission electron microscope), phases (X ray diffraction), roughness (atomic force microscope) and mechanical properties (microhardness and tensile) were analyzed for cast, MDF processed and MDF + ball burnished samples. The study also defines a new reliability simulation framework to predict the roughness and hardness of the MDF + ball burnished samples using Deep Neural Network (DNN) approach. For the analysis, depth of press, feed and number of passes served as inputs for the DNN model. After configuring and training procedure of the model, the predicted roughness and microhardness of the MDF + ball burnished were compared with the results of experimental data. A large increase of microhardness was observed for MDF-5 + BB-1 (5 pass MDF processed Mg-2%Zn alloy + Ball burnished sample), found to be 98 Hv and surface roughness of 306 nm was achieved. According to the results, the obtained R-squared value is very close to the 99.5 percentage from the model for predicting roughness and hardness which is a promising result. Corrosion behavior of the AS-1, MDF-5 and MDF-5 + BB-1 was evaluated in Hank's balanced salt solution. Corrosion rate of the MDF-5 + BB-1 samples were found to be 0.87 mm/y which is 7 times better than that of AS-1 samples (6.10 mm/y). Grain refinement and residual stresses were higher in the MDF-5 + BB-1 sample, which helped significantly to enhance corrosion resistance. © 2021 The Society of Manufacturing EngineersItem Enhancing surface characteristics of Mg-Zn-Sr alloy through cryo-ball burnishing; modeling and experimentation(Korean Society of Mechanical Engineers, 2024) Kudva, S.A.; Anne, G.; Ramesh, S.; Sharma, P.; Jagadeesh, C.; Ritti, L.; Naik, G.M.; Divya Deepak, G.D.In this investigation, the impact of the cryo-ball burnishing process on both the mechanical and corrosion properties of the Mg-4Zn-1Sr alloy was systematically explored. To better understand the plastic deformation occurring in Mg-4Zn-1Sr during cryo-burnishing, a finite element analysis (FEA) model was developed. The microstructure of cryo-ball burnished samples underwent characterization through scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray diffractometry (XRD), and surface properties were assessed using atomic force microscopy (AFM). Additionally, electrochemical impedance spectroscopy and potentiodynamic polarization tests were conducted in a simulated body fluid using an electrochemical workstation. Experimental findings revealed significant grain refinement and the presence of residual dislocations during the cryo-burnishing process, as evident in TEM analysis. XRD analysis indicated the presence of Mg, Mg17Sr2 and SrZn2 phases, with observable peak broadening in the cryo-burnished samples, attributed to structural refinement and lattice strain incorporation. Microhardness values increased with greater depth of press, with the DFN 1071 sample displaying a hardness of 80 ± 4 Hv (Ra = 1.853 µm), marking a 54 % improvement compared to the homogenized sample. The enhanced corrosion resistance of the Mg-4Zn-1Sr alloy due to cryo-burnishing is attributed to the combined effects of grain refinement, residual dislocations, and intermetallic phases. © The Korean Society of Mechanical Engineers and Springer-Verlag GmbH Germany, part of Springer Nature 2024.Item Effect of addition of Ce and accumulative roll bonding on structure-property of the Mg-Ce-Al hybrid composite and its prediction and comparison using artificial neural network (ANN) approach(Institute of Physics, 2024) Anne, G.; Bhat, N.; Vishwanatha, H.M.; Ramesh, S.; Maruthi Prashanth, B.H.; Sharma, P.; Aditya Kudva, S.; Jagadeesh, C.; Nanjappa, Y.Light alloys play a crucial role in realizing the national strategy for energy conservation and emission reduction, as well as promoting the upgrading of manufacturing industries. Mg/Al composite laminates combine the corrosion resistance and ductility of aluminium alloy with the lightweight characteristics of magnesium alloy. The addition of Ce (rare earth elements) can improve the mechanical properties of magnesium via grain refinement and improve the ductility of the hybrid composites. In the present work, an investigation on addition of Ce into the Mg/Al matrix through Accumulative Roll Bonding (ARB) has been presented. The Mg/Ce/Al hybrid composite consists of Mg-4%Zn alloy and Al 1100 alloy with 0.2% Ce particles added between the dissimilar layers. The changes occurred in the evaluation of microstructure, corrosion and mechanical properties of the Mg/Ce/Al hybrid composite as a result of deformation process and also the addition of Ce have been explicated. The ARB parameters: temperature, rolling speed, percentage reduction, and aging time, have been studied. An increase of about 2.36 times in strength and hardness of the hybrid composite, has been reported. Further, the structure-property relations in the Mg/Ce/Al hybrid composites were aslo predict and compare using machine learning models: Decision Tree and Multi-Layer Perceptron (MLP) models. © 2024 The Author(s). Published by IOP Publishing Ltd.Item Combined effect of multidirectional forging and heat treatment on erosion and corrosion behaviour of the Mg-Zn-Mn alloys(Korean Society of Mechanical Engineers, 2024) Anne, G.; Hegde, A.; Kudva, S.A.; Sharma, P.; Kumar, P.; Matapati, M.; Ramesh, S.; Sharma, S.S.Multidirectional forging (MDF) was successfully applied to the Mg-4Zn-1Mn alloy for five passes at 300 °C. The grain size of 5 pass MDF processed samples reached 18 ± 3 µm from 256 ± 6 µm, and ?-Mg, MgZn2 and MnZn13 peaks were observed. Further MDF processed samples were solution treated (ST) at 300 °C for 2 h and quenched in SAE 20W40 oil and followed by artificial ageing (A) at 170 °C for four different timings including 1.5 h, 2 h, 2.5 h and 3.5 h respectively. The peak hardness of 219 Hv (5 pass MDF + H sample) was found in 2h artificial ageing which is 3.1 times higher compared to counterpart homogenised samples. Improvement of mechanical properties was attributed to smaller grain size and precipitation strengthening as well as distribution of the secondary phases. The combined effect of MDF and heat treatment was analysed using solid particle erosion tests at 30° and 90° impact angles using alumina. It was observed that higher impact angle (90°) had more erosion rate in all conditions and 5 pass MDF + H samples exhibited better erosion (0.0001 mg/g) due to higher hardness. On the other hand, polarisation and electrochemical impedance spectroscopy measurements were used to assess the alloys’ corrosion behaviour. The 3 pass MDF + H sample was found to have a corrosion rate of 0.0235 mm/y, which is two times lower than the counterpart 3 pass MDF processed samples and sixteen times lower than the homogenised sample (0.3838 mm/y). This was primarily due to the secondary phases’ better distribution and smaller grain size. © The Korean Society of Mechanical Engineers and Springer-Verlag GmbH Germany, part of Springer Nature 2024.