Faculty Publications
Permanent URI for this communityhttps://idr.nitk.ac.in/handle/123456789/18736
Publications by NITK Faculty
Browse
Search Results
Item Examining the Influence of StackinSequence on the Mechanical Properties of Hybrid Abaca-Jute Vinyl Ester Composites(Springer Nature, 2024) Ramesh, S.; Maruthi Prashanth, B.H.; Anne, G.; Naik, G.M.; Reddy, R.; Jagadeesh, C.; Sharma, P.; Prashanth Pai, M.This research looked on the impacts of layer arrange-ment on inter-laminar shear strength (ILSS), tensile, flexural, and impact capabilities of hybrid composite developed from 25% abaca and 25% jute fabrics reinforced 50% vinyl ester. Furthermore, the samples frac-tured under the tensile load were examined using SEM images. Utilizing a hot press process, these hybrid laminates were fabricated and sample preparation and testing were done as per ASTM criteria. The findings demonstrate that among Abaca-Jute-Abaca-Jute (AJAJ), Abaca-Jute-Abaca (AJJA), and Jute-Abaca-Abaca-Jute (JAAJ) vinyl ester composites, the Abaca-Jute-Jute-Abaca (AJJA) composites showed higher tensile modulus and strength by 23–33%, the flexural modulus and strength by 3–22%, the impact behavior, and ILSS strength by 11–33%. These benefits could be attributed to the presence of abaca fiber on the exterior of lami-nates. Fractography studies revealed that the fiber-resin bonding was superior. AJJA composites were found to be stronger than commonly used plastics in automobile interiors, making them a promising alternative. © The Author(s), under exclusive license to Springer Nature Switzerland AG 2024.Item Impact of ply stacking sequence on the mechanical response of hybrid Jute-Banana fiber phenoplast composites(Institute of Physics, 2024) Maruthi Prashanth, B.H.; Ramesh, S.; Shivakumar Gouda, P.S.S.; Naik, G.M.; Sharma, P.; Jagadeesh, C.; Mahantesh, M.M.; Anne, G.Natural fiber composites are increasingly gaining popularity as a cost-effective and environmentally friendly alternative to synthetic fibers. Incorporating a variety of fibers enhances mechanical properties. The arrangement of fibers plays a crucial role in determining the mechanical characteristics of laminate composites. Therefore, the primary objective of this study is to investigate how the stacking order of jute (J) and banana (B) fibers affects the mechanical behaviour of composites made from phenolic resins. Four different fiber mat stacking sequences (J/B/B/J, B/J/J/B, J/B/J/B, and J/J/B/B) were used for developing the eco-fiber composites using the heat-press technique. Several mechanical parameters were assessed, including tensile strength, flexural strength, impact strength, and inter-laminar shear strength (ILSS). The experimental results indicated that the JBBJ composite exhibits superior tensile strength (46.65 MPa) and modulus (993 MPa) compared to the other composites due to the presence of high-strength jute fibers on the surface. Additionally, the flexural strength of the JBBJ composite (87.24 MPa) was found to be noteworthy. It was observed that the impact strength of jute fibers surpasses that of banana fibers. Consequently, the JBBJ composite demonstrates higher values for energy absorption (0.482 J) and impact strength (120 J m−1) compared to the other composites tested. Moreover, the JBBJ composite displays higher inter-laminar shear strength and hardness values compared to BJJB, JBJB, and JJBB by 30%, 35%, and 43%, respectively. Scanning electron microscope microphotographs reveal strong correlational fracture failure mechanisms, indicative of improved mechanical properties in the JBBJ composite. Based on the experimental results, it is evident that the JBBJ composite can be utilized in lightweight applications. © 2024 The Author(s). Published by IOP Publishing Ltd.