Faculty Publications
Permanent URI for this communityhttps://idr.nitk.ac.in/handle/123456789/18736
Publications by NITK Faculty
Browse
Search Results
Item Use of Stabilized Lateritic and Black Cotton Soils as a Base Course Replacing Conventional Granular Layer in Flexible Pavement(Springer, 2020) Amulya, S.; Ravi Shankar, A.U.The present work investigates the improved properties of lateritic and black cotton soils stabilized with ground granulated blast furnace slag (GGBFS) and alkali solutions. The alkali solution includes a mixture of sodium hydroxide and sodium silicate. The lateritic and black soils are treated with 30% GGBFS and the alkali solutions consisting of 6% Na2O having silica modulus (Ms) of 0.5, 1.0 and 1.5 at a constant water binder ratio of 0.25. The treated samples were air-cured for 0 (immediately after casting), 3, 7 and 28 days at ambient temperature. The treated lateritic soil with 0.5 and 1.0 Ms is found durable after 3, 7, and 28 days curing. Whereas, the treated BC soil found durable with Ms 0.5 at modified Proctor density after 28 days curing. The formation of calcium silicate hydrate and calcium aluminosilicate hydrate structures resulted in a remarkable improvement of compressive strength, flexure and fatigue life of treated soils due to dissolved calcium ions from GGBFS, silicate and aluminium ions from alkali solutions. The microstructure image of the durable soil sample shows the crystal orientation of particles. The design of high and low volume roads is proposed by replacing the conventional granular layer with the durable stabilized soil and stress–strain analysis is carried out using pavement analysis software. © 2020, Springer Nature Switzerland AG.Item Replacement of Conventional Base Course with Stabilized Lateritic Soil Using Ground Granulated Blast Furnace Slag and Alkali Solution in the Flexible Pavement Construction(Springer, 2020) Amulya, S.; Ravi Shankar, A.U.The use of cement/chemical-treated base and sub-bases is widely recommended in the pavement construction. Therefore, this paper investigates the behaviour of stabilized lateritic soil as a base course in flexible pavement by replacing the granular base course. The lateritic soil was stabilized with 25% Ground Granulated Blast Furnace Slag (GGBFS) along with the alkali solutions such as sodium hydroxide and sodium silicate at a varying sodium oxide (Na2O) contents of 4, 5 and 6%, silica modulus (Ms, a ratio of silica to sodium oxide) of 0.5, 1.0 and 1.5 and a constant water binder ratio (w/b) of 0.25. The maximum compressive strengths of 5452 and 6593 kPa were achieved for a treated sample consisting of 6% Na2O and 1.0 Ms cured for 28 days at the light and heavy compactions, respectively, which is due to the formation of calcium silicate hydrates when calcium oxide-rich GGBFS reacts with water. Further with the curing period results in an increase in strength due to the formation of calcium alumino-silicate hydrates when GGBFS reacts with alkali solutions. The durability of the samples was evaluated by wetting–drying and freezing–thawing tests. The samples passing the required durability criteria were tested for flexural strength and fatigue life. Scanning electron microscope images showed closely packed crystal orientation indicating high strength. Low and high volume pavements were designed using stabilized soil as a base course, and the strains were evaluated using pavement analysis software. It is suggested that the conventional granular base layer can be replaced with the stabilized soil. © 2020, Indian Geotechnical Society.