Faculty Publications
Permanent URI for this communityhttps://idr.nitk.ac.in/handle/123456789/18736
Publications by NITK Faculty
Browse
3 results
Search Results
Item Electroactive poly(vinylidene fluoride) fluoride separator for sodium ion battery with high coulombic efficiency(Elsevier B.V., 2016) Janakiraman, S.; Surendran, A.; Ghosh, S.; Anandhan, S.; Adyam, A.Electroactive separators are recent interest in self-charging rechargeable batteries. In this study, electrospun polyvinylidene fluoride (PVDF) is characterized as an electroactive separator for Na-ion batteries. The intrinsic ?-phase with high porosity of the separator is confirmed from X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), Field emission scanning electron microscopy (FESEM) and Atomic Force Microscopy (AFM) studies. The electroactive separator is immersed in 1M NaClO4-ethylene carbonate (EC)/diethyl carbonate (DEC) (1:1 by weight) solution. The physicochemical characteristics of electroactive separator electrolyte (EaSE) were investigated using sodium ion conductivity, ion transference number and contact angle measurements. Linear and cyclic voltammetry studies were also carried out for the electrolyte system to evaluate oxidation stability window. The inherent ?-phases of the separator as obtained by electrospinning has an ionic conductivity of ~ 7.38 × 10- 4 S cm- 1 under ambient condition. Sodium ion cell made from EaSE with Na0·66Fe0.5Mn0·5O2 as cathode and Na metal as anode has displayed a stable cycle performance with a coulombic efficiency of 92% after 90 cycles. © 2016 Published by Elsevier B.V.Item A new strategy of PVDF based Li-salt polymer electrolyte through electrospinning for lithium battery application(Institute of Physics Publishing helen.craven@iop.org, 2019) Janakiraman, S.; Surendran, A.; Ghosh, S.; Anandhan, S.; Adyam, A.Polyvinylidene fluoride (PVDF) ultrafine fibers with different proportions of lithium nitrate (LiNO3) were fabricated by an electrospinning device. The processing parameters are optimized to 19 wt% PVDF to get a bead free structure. Scanning electron microscope (SEM) and atomic force microscope (AFM) showed the uniform and interconnected porous structure. With the addition of 2 wt% LiNO3, the fiber diameter of the electrospun membrane decreased from 371 to 222 nm. Furthermore, the addition of LiNO3 into the nanofibrous membrane enhanced the ionic conductivity from 0.97 ×10-3 S cm-1 to 1.61 ×10-3 S cm-1 at room temperature after soaking with 1 M LiPF6 (lithium hexafluoro-phosphate) in ethylene carbonate (EC) and diethyl carbonate (DEC) in (1:1 wt%). Compared with the conventional Celgard and pristine PVDF membrane, the salt doped PVDF membranes showed higher electrochemical stability window and lower interfacial resistance. The electrospun membrane separators (ES) were assembled into Lithium cobalt oxide (LiCoO2) as cathode and lithium metal as an anode. The salt doped membrane showed superior discharge, C-rate and stable cycle performance than the commercial Celgard membrane. © 2018 IOP Publishing Ltd.Item Electrospun electroactive polyvinylidene fluoride-based fibrous polymer electrolyte for sodium ion batteries(Institute of Physics Publishing helen.craven@iop.org, 2019) Janakiraman, S.; Surendran, A.; Biswal, R.; Ghosh, S.; Anandhan, S.; Adyam, A.Electrospinning is an efficient technique to produce ultrafine electroactive mat, diameters ranging from few nanometers to micrometers to use as a separator in sodium ion battery. The polyvinylidene fluoride (PVDF) polymer solution was optimized to 19 wt%, applied voltage 25 kV and flow rate of 0.5 ml h-1 to get a bead free ultrafine electroactive structure. The electroactive ?-phase is confirmed by x-ray diffractometer (XRD). Ionic conductivities, electrolyte uptake, wettability, linear sweep voltammetry (LSV) and thermal stability of the electroactive fibrous polymer electrolyte (EFPE) were studied by soaking the separator with a liquid electrolyte of 1 M sodium hexafluorophosphate (NaPF6) dissolved in ethylene carbonate (EC)/propylene carbonate (PC) (1:1 vol%). The EFPE exhibits high ionic conductivity of 1.08 mS cm-1 and electrochemical stability window of 5.0 V versus Na/Na+ under ambient condition. The half-cell containing Na0.66Fe0.5Mn0.5O2 as cathode and EFPE as the separator cum electrolyte showed a stable cycling performance at a current rate of 0.1C. © 2019 IOP Publishing Ltd.