    Effect of Wire Material on Productivity and Surface Integrity of WEDM-Processed Inconel 706 for Aircraft Application
    (Springer New York LLC barbara.b.bertram@gsk.com, 2016) Sharma, P.; Dupadu, D.; Narendranath, S.
    Inconel 706 is a recently developed superalloy for aircraft application, particularly in turbine disk which is among the most critical components in the gas turbine engines. Recently, wire electrical discharge machining (WEDM) attained success in machining of gas turbine components which require complex shape profiles with high precision. To achieve the feasibility in machining of these components, the research work has been conducted on Inconel 706 superalloy using WEDM process. And, the effect of different wire materials (i.e., hard brass wire, diffused wire, and zinc-coated wire) on WEDM performance characteristics such as cutting speed, surface topography, surface roughness, recast layer formation, residual stresses, and microstructural and metallurgical alterations have been investigated. Even though, zinc-coated wire exhibits improved productivity, hard brass wire was found to be beneficial in terms of improved surface quality of the machined parts. Additionally, lower tensile residual stresses were obtained with hard brass wire. However, diffused wire has a moderate effect on productivity and surface quality. Under high discharge energy, higher elemental changes were observed and also the white layer was detected. © 2016, ASM International.
  • No Thumbnail Available
    Item
    Corrosion resistance and in-vitro bioactivity of BaO containing Na2O-CaO-P2O5 phosphate glass-ceramic coating prepared on 316 L, duplex stainless steel 2205 and Ti6Al4V
    (Institute of Physics Publishing helen.craven@iop.org, 2018) Edathazhe, A.B.; Shashikala, H.D.
    The phosphate glass with composition 11Na2O-15BaO-29CaO-45P2O5 was coated on biomedical implant materials such as stainless steel 316 L, duplex stainless steel (DSS) 2205 and Ti6Al4V alloy by thermal enamelling method. The structural properties and composition of glass coated substrates were studied by x-ray diffraction (XRD), Scanning electron microscopy (SEM) and Energy dispersive x-ray spectroscopy (EDS) analysis. The coatings were partially crystalline in nature with porous structure and pore size varied from micro to nanometer range. The polarization curve was obtained for uncoated and coated substrates from electrochemical corrosion test which was conducted at 37 °C in Hank's balanced salt solution (HBSS). The corrosion resistance of 316 L substrate increased after coating, whereas it decreased in case of DSS 2205 and Ti6Al4V. The XRD and SEM/EDS studies indicated the bioactive hydroxyapatite (HAp) layer formation on all the coated surfaces after electrochemical corrosion test, which improved the corrosion resistance. The observed electrochemical corrosion behavior can be explained based on protective HAp layer formation, composition and diffusion of ions on glass coated surfaces. The in-vitro bioactivity test was carried out at 37 °C in HBS solution for 14 days under static conditions for uncoated and coated substrates. pH and ion release rate measurements from the coated samples were conducted to substantiate the electrochemical corrosion test. The lower ion release rates of Na+ and Ca2+ from coated 316 L supported its higher electrochemical corrosion resistance among coated samples. Among the uncoated substrates, DSS showed higher electrochemical corrosion resistance. Amorphous calcium-phosphate (ACP) layer formation on all the coated substrates after in-vitro bioactivity test was confirmed by XRD, SEM/EDS and ion release measurements. The present work is a comparative study of corrosion resistance and bioactivity of glass coated and uncoated biomedical implants such as 316 L, DSS and Ti6Al4V. © 2018 IOP Publishing Ltd.
  • No Thumbnail Available
    Item
    Microstructure and Adhesion Strength of Ni3Ti Coating Prepared by Mechanical Alloying and HVOF
    (Pleiades Publishing compmg@maik.ru, 2018) Reddy, N.C.; Ajay Kumar, B.S.; Ramesh, M.R.; Koppad, P.G.
    In the present work we report the development of Ni3Ti intermetallic compound by high energy ball milling of Ni and Ti powders. The ball milled powders were taken at various intervals (4, 6, 8, 10, and 11 h) to analyze the formation of NixTix intermetallic compounds. The ball milled powders were analyzed using scanning electron microscopy and X-ray diffraction. The layered shaped powder particles of Ni3Ti phase were formed after 11 h of ball milling, which was confirmed by X-ray peaks. Further High-Velocity Oxy-Fuel (HVOF) process was used to coat Ni3Ti and Ni3Ti + (Cr3C2 + 20NiCr) on MDN 420 steel. Both the coated materials displayed excellent cohesion with minimal porosity less than 2%. The tensile adhesion strength test was carried out on these coatings to check the bond strength. Out of the two the Ni3Ti coating showed excellent bond strength of 41.04 MPa compared to that of Ni3Ti + (Cr3C2 + 20NiCr) coating. © 2018, Pleiades Publishing, Ltd.
  • No Thumbnail Available
    Item
    Hot corrosion behaviour of HVOF sprayed Ni3Ti and Ni3Ti + (Cr3C2 + 20NiCr) coatings in presence of Na2SO4-40%V2O5 at 650 °c
    (IOP Publishing Ltd custserv@iop.org, 2019) Reddy, N.C.; Koppad, P.G.; Reddappa, H.N.; Ramesh, M.R.; Babu, E.R.; Varol, T.
    Ni3Ti and Ni3Ti + (Cr3C2 + 20NiCr) coatings were deposited on gas turbine based ASTM B265 titanium (Ti-15) and AISI 420 stainless steel (MDN-420) substrate materials using HVOF technique. Thermocyclic hot corrosion tests were carried out at 650 °C in molten salt environment of Na2SO4-40%V2O5 for about 50 cycles. Thermogravimetric analysis was carried out to study the hot corrosion kinetics of uncoated and coated titanium and stainless steel substrates. The weight gain per unit area showed that the coated substrate materials displayed better resistance to hot corrosion when compared with that of uncoated substrate materials. The surface morphology of uncoated and coated substrate materials were analysed using scanning electron microscopy and elemental analysis. The formation of different types of oxides and compounds were analysed using x-ray diffraction. The uncoated substrates surface showed microspalling at several regions while coated substrates surface were composed of protective oxide layers. The presence of ternary NiCr2O4 protective oxides on the surface of Ni3Ti + (Cr3C2 + 20NiCr) coated substrates leads to reduction in the diffusion of corrosive species inside the coating. © 2019 IOP Publishing Ltd.