Journal Articles
Permanent URI for this collectionhttps://idr.nitk.ac.in/handle/123456789/19884
Browse
4 results
Search Results
Item Effect of purging gas on wetting behavior of Sn-3.5Ag lead-free solder on nickel-coated aluminum substrate(Springer Science and Business Media, LLC, 2013) Prabhu, K.; Varun, M.; Satyanarayan, S.The wetting characteristics of Sn-3.5Ag lead-free solder alloy on nickel-coated aluminum substrates in air (ambient), nitrogen, and argon atmospheres were investigated. The contact angles for the solder alloy obtained under air and argon atmospheres were in the range of 36 -38. With nitrogen atmosphere the contact angle was found to be significantly lower at about 26. Solder solidifying in air exhibited needle-shaped tin-rich dendrites surrounded by a eutectic matrix. The amount of tin dendrites decreased in argon atmosphere. However, the morphology of tin dendrites transformed from needle-shaped to nearly non-dendritic shape as the soldering atmosphere was changed from air to nitrogen. The interfacial microstructures revealed the presence of Ni 3Sn and Ni3Sn4 IMCs at the interface. The enhanced wettability observed under nitrogen atmosphere is attributed to the higher thermal conductivity of nitrogen gas and the formation of higher amount of Ni3Sn IMCs at the interface compared to air and argon atmospheres. © 2012 ASM International.Item Spreading behavior and evolution of IMCs during reactive wetting of SAC solders on smooth and rough copper substrates(2013) Satyanarayan, S.; Prabhu, K.The effect of surface roughness of copper substrate on the reactive wetting of Sn-Ag-Cu solder alloys and morphology of intermetallic compounds (IMCs) was investigated. The spreading behavior of solder alloys on smooth and rough Cu substrates was categorized into capillary, diffusion/reaction, and contact angle stabilization zones. The increase in substrate surface roughness improved the wetting of solder alloys, being attributed to the presence of thick Cu 3Sn IMC at the interface. The morphology of IMCs transformed from long needle shaped to short protruded type with an increase in the substrate surface roughness for the Sn-0.3Ag-0.7Cu and Sn-3Ag-0.5Cu solder alloys. However, for the Sn-2.5Ag-0.5Cu solder alloy the needle-shaped IMCs transformed to the completely scallop type with increase in the substrate surface roughness. The effect of Ag content on wetting behavior was not significant. © 2013 TMS.Item Solder joint reliability of Sn-0·7Cu and Sn-0·3Ag- 0·7Cu lead-free solder alloys solidified on copper substrates with different surface roughnesses(2013) Satyanarayan, S.; Prabhu, K.The bond shear test was used to assess the integrity of Sn-0·7Cu and Sn-0·3Ag-0·7Cu lead-free solder alloy drops solidified on copper substrates with smooth and rough surface finishes. Solder alloys solidified on smooth substrates required higher shear force compared to that on rough substrates. Sn-0·3Ag-0·7Cu alloy required higher shear energy than Sn-0·7Cu alloy. Solder alloys solidified on smooth substrate surfaces exhibited complete ductile failure. On rough copper surfaces, solder alloys showed a transition ridge characterized by sheared intermetallic compounds (IMCs) and the presence of dimples. The peak shear strength decreased with increase in contact area of the solder bond on the substrate. Smooth surface and the presence of minor amount of Ag in the solder alloy enhance the integrity of the solder joint. © 2013 Institute of Materials, Minerals and Mining.Item Effect of cooling rate on joint shear strength of Sn-9Zn lead-free solder alloy reflowed on copper substrate(ASTM International, 2017) Tikale, S.; Sona, M.; Prabhu, K.Reliability of the solder joint largely depends on mechanical strength, fatigue resistance, coefficient of thermal expansion, and intermetallic compound formation. Cooling rate significantly affects the physical properties of an alloy and influences the mechanical behavior of solder joints. In the present study, Sn-9Zn lead-free solder alloy was solidified on Cu substrate under furnace cooling (0.04°C/s), air cooling (0.16°C/s), and water cooling (94°C/s) conditions. The effect of varying cooling rates on the intermetallic compound (IMC) formation at the interface and the resulting joint shear strength was studied. A microstructure study revealed the presence of Cu5Zn8 and CuZn5 intermetallic compounds at the solder-substrate interface. The IMC layer thickness at the interface increased with a decrease in the cooling rate. The joint shear strength increased with an increase in the cooling rate. The air and furnace cooling resulted in the formation of a thick IMC layer. The IMC obtained from the furnace cooling was associated with micro-cracks leading to a decrease in the joint shear strength. © Copyright 2017 by ASTM International.