Methanol selective oxidation to formaldehyde over a modified Fe-Mo catalyst with two different stoichiometric (Mo/Fe atomic ratio = 1.5 and 3.0) was studied experimentally in a fixed bed reactor over a wide range of reaction conditions. The physicochemical characterization of the prepared catalysts provides evidence that Fe2(MoO4)3 is in fact the active phase of the catalyst. The experimental results of conversion of methanol and selectivity towards formaldehyde for various residence times were studied. The results showed that as the residence time increases the yield of formaldehyde decreases. Selectivity of formaldehyde decreases with increase in residence time. This result is attributable to subsequent oxidation of formaldehyde to carbon monoxide due to longer residence time.
(Selective oxidation of methanol to formaldehyde using modified iron-molybdate catalysts) Kim, T.-H.; Badekai Ramachandra, B.; Choi, J.-S.; Saidutta, M.B.; Choo, K.-Y.; Song, S.-D.; Rhee, Y.-W.
2004
Molybdenum based mixed oxide containing Mo0.65V 0.25W0.10 was investigated for the partial oxidation of methanol. The structural property and catalytic activity of the mixed oxide catalyst was studied by surface area (BET), scanning electron microscopy (SEM), energy dispersive X-ray (EDX), Fourier transform infra-red spectroscopy (FTIR) and X-ray diffraction (XRD). The thermal activation of the catalyst resulted increase in the conversion of methanol and the selectivity to formaldehyde. The thermal activation of the MoVW mixed oxide in nitrogen atmospheres induces partial crystallization of a Mo5O14-type oxide at 813 K. The SEM images of the thermally activated catalyst show needle like particles. These particles were agglomerates of platelet-like crystallites of a few hundreds of nanometers in size. SEM and EDX techniques show that the mixed oxide is characterized by an inhomogeneous elemental distribution on the length scale of a few microns. XRD of the thermally activated catalyst showed a nanocrystalline material identified as a mixture of Mo5O 14, MoO3 and MoO2-type MoVW oxides. The catalytic activity of the MoVW mixed oxide show a good conversion of methanol and selectivity to formaldehyde. © 2005 Springer Science+Business Media, Inc.
(Partial oxidation of methanol to formaldehyde on molybdenum based mixed oxide catalyst) Badekai Ramachandra, B.; Choi, J.-S.; Choo, K.-Y.; Sung, J.-S.; Song, S.-D.; Kim, T.-H.
2005