Comparison of structural health assessment capabilities in epoxy - Carbon black and epoxy - Carbon nanotube nanocomposites
(2014) Inam, F.; Bhat, B.R.; Luhyna, N.; Vo, T.
A novel method for comparing structural health of different types of brittle epoxy nanocomposites filled with carbon nanostructured fillers is presented. Epoxy - 0.2 vol% carbon black (CB) and epoxy - 0.2 vol% carbon nanotube (CNT) nanocomposite bars were prepared by calendering and thermal curing. Nanocomposite bars were subjected to Vickers diamond indentation to produce sub-surface damage. Electrical conductivities were analysed by 4-point method to estimate the structural damage caused by indentation. For comprehensive comparison, fracture toughness and percolation threshold were analysed as well. Because of the systematically induced indentation damage, a sharp decrease of 89% was observed in the electrical conductivity of epoxy - CNT nanocomposite as compared to 25% in the electrical conductivity of epoxy - CB nanocomposite. CNTs impart superior damage sensing capability in brittle nanocomposite structures, in comparison to CB, due to their high aspect ratio (fibrous nature) and high electrical conductivity. BME-PT.
Comparison of structural health assessment capabilities in epoxy - Carbon black and epoxy - Carbon nanotube nanocomposites
(2014) Inam, F.; Badekai Ramachandra, B.; Luhyna, N.; Vo, T.
A novel method for comparing structural health of different types of brittle epoxy nanocomposites filled with carbon nanostructured fillers is presented. Epoxy - 0.2 vol% carbon black (CB) and epoxy - 0.2 vol% carbon nanotube (CNT) nanocomposite bars were prepared by calendering and thermal curing. Nanocomposite bars were subjected to Vickers diamond indentation to produce sub-surface damage. Electrical conductivities were analysed by 4-point method to estimate the structural damage caused by indentation. For comprehensive comparison, fracture toughness and percolation threshold were analysed as well. Because of the systematically induced indentation damage, a sharp decrease of 89% was observed in the electrical conductivity of epoxy - CNT nanocomposite as compared to 25% in the electrical conductivity of epoxy - CB nanocomposite. CNTs impart superior damage sensing capability in brittle nanocomposite structures, in comparison to CB, due to their high aspect ratio (fibrous nature) and high electrical conductivity. © BME-PT.
Structural health monitoring capabilities in ceramic-carbon nanocomposites
(2014) Inam, F.; Bhat, B.R.; Vo, T.; Daoush, W.M.
A novel method for analysing structural health of alumina nanocomposites filled with graphene nanoplatelets (GNP), carbon nanotubes (CNTs) and carbon black nano-particles (CB) is presented. All nanocomposites were prepared using novel colloidal processing and then by Spark Plasma Sintering. Good homogeneous dispersion was observed for all carbon filled materials. Nanocomposite bars were indented to produce sub-surface damage. Change in electrical conductivities were analysed after indentation to understand structural damage. For correlating change in electrical conductivity and indentation damage and understanding damage tolerance, mechanical properties were compared. Because of the systematically induced indentation damage, a sharp decrease of 86% was observed in the electrical conductivity of CNT nanocomposite as compared to 69% and 27% in the electrical conductivities of GNP nanocomposites and CB nanocomposites respectively. CNTs impart superior damage sensing capability in alumina nanocomposites, in comparison to GNP and CB, due to their fibrous nature, high aspect ratio and high electrical conductivity. 2013 Elsevier Ltd and Techna Group S.r.l.
Structural health monitoring capabilities in ceramic-carbon nanocomposites
(2014) Inam, F.; Badekai Ramachandra, B.R.; Vo, T.; Daoush, W.M.
A novel method for analysing structural health of alumina nanocomposites filled with graphene nanoplatelets (GNP), carbon nanotubes (CNTs) and carbon black nano-particles (CB) is presented. All nanocomposites were prepared using novel colloidal processing and then by Spark Plasma Sintering. Good homogeneous dispersion was observed for all carbon filled materials. Nanocomposite bars were indented to produce sub-surface damage. Change in electrical conductivities were analysed after indentation to understand structural damage. For correlating change in electrical conductivity and indentation damage and understanding damage tolerance, mechanical properties were compared. Because of the systematically induced indentation damage, a sharp decrease of 86% was observed in the electrical conductivity of CNT nanocomposite as compared to 69% and 27% in the electrical conductivities of GNP nanocomposites and CB nanocomposites respectively. CNTs impart superior damage sensing capability in alumina nanocomposites, in comparison to GNP and CB, due to their fibrous nature, high aspect ratio and high electrical conductivity. © 2013 Elsevier Ltd and Techna Group S.r.l.
Structural stability studies of graphene in sintered ceramic nanocomposites
(2014) Inam, F.; Vo, T.; Bhat, B.R.
The post-sintering structural stability of graphene in alumina nanocomposites synthesised by Spark Plasma Sintering (SPS) and Hot Pressing (HP) was compared. Raman spectroscopy, thermogravimetric analyses and electrical conductivity analyses were conducted to characterise degradation of graphene due to the utilisation of different sintering techniques and conditions. Scanning Electron Microscopy confirmed good dispersion of graphene in SPSed and HPed sample. Graphene in SPSed and HPed nanocomposite samples sintered using longer durations (60 min) were found to possess higher crystallinity, thermal stability and electrical conductivity as compared to SPSed samples sintered using shorter sintering durations (10-20 min). This was attributed to the thermally induced graphitisation caused by longer sintering durations, which was lacking in SPSed samples processed using shorter sintering durations and lower temperature. No additional effect of DC pulsed current on the structural stability of graphene for nanocomposites were observed for samples prepared by SPS. 2014 Elsevier Ltd and Techna Group S.r.l.
Structural stability studies of graphene in sintered ceramic nanocomposites
(Elsevier Ltd, 2014) Inam, F.; Vo, T.; Badekai Ramachandra, B.R.
The post-sintering structural stability of graphene in alumina nanocomposites synthesised by Spark Plasma Sintering (SPS) and Hot Pressing (HP) was compared. Raman spectroscopy, thermogravimetric analyses and electrical conductivity analyses were conducted to characterise degradation of graphene due to the utilisation of different sintering techniques and conditions. Scanning Electron Microscopy confirmed good dispersion of graphene in SPSed and HPed sample. Graphene in SPSed and HPed nanocomposite samples sintered using longer durations (60 min) were found to possess higher crystallinity, thermal stability and electrical conductivity as compared to SPSed samples sintered using shorter sintering durations (10-20 min). This was attributed to the thermally induced graphitisation caused by longer sintering durations, which was lacking in SPSed samples processed using shorter sintering durations and lower temperature. No additional effect of DC pulsed current on the structural stability of graphene for nanocomposites were observed for samples prepared by SPS. © 2014 Elsevier Ltd and Techna Group S.r.l.