Chitosan/NiO nanocomposites: A potential new dielectric material
(2011) Bhatt, A.S.; Bhat, D.K.; Santosh, M.S.; Tai, C.-W.
The study of electrochemical behavior of organic-inorganic nanocomposite materials remains a major challenge for application in energy storage devices. Here, new composite materials of chitosan and NiO nanoparticles have been fabricated. The NiO nanoparticles are well characterized by infrared spectroscopy, X-ray diffraction and transmission electron microscopy. The electrical properties of the films are studied by impedance spectroscopy at different temperatures; and thereby permittivity, electric modulus and conductivity data are obtained. By studying the variations in permittivity and electric modulus spectra with respect to applied frequency signal and temperature, the ionic conductivity of the material is investigated. The Correlated Barrier Hopping model is employed to understand the conduction mechanism. An admirable conductivity of 1.4 10-2 S cm -1 is obtained for a nanocomposite with 4 wt% NiO content. The activation energies of the composite films decrease with increase in NiO content, from 16.5 to 4.8 kJ mol-1. 2011 The Royal Society of Chemistry.
Chitosan/NiO nanocomposites: A potential new dielectric material
(2011) Bhatt, A.S.; Bhat, D.K.; Santosh, M.S.; Tai, C.-W.
The study of electrochemical behavior of organic-inorganic nanocomposite materials remains a major challenge for application in energy storage devices. Here, new composite materials of chitosan and NiO nanoparticles have been fabricated. The NiO nanoparticles are well characterized by infrared spectroscopy, X-ray diffraction and transmission electron microscopy. The electrical properties of the films are studied by impedance spectroscopy at different temperatures; and thereby permittivity, electric modulus and conductivity data are obtained. By studying the variations in permittivity and electric modulus spectra with respect to applied frequency signal and temperature, the ionic conductivity of the material is investigated. The Correlated Barrier Hopping model is employed to understand the conduction mechanism. An admirable conductivity of 1.4 × 10-2 S cm -1 is obtained for a nanocomposite with 4 wt% NiO content. The activation energies of the composite films decrease with increase in NiO content, from 16.5 to 4.8 kJ mol-1. © 2011 The Royal Society of Chemistry.
Microwave-assisted synthesis and magnetic studies of cobalt oxide nanoparticles
(2011) Bhatt, A.S.; Bhat, D.K.; Tai, C.-W.; Santosh, M.S.
An efficient microwave-assisted route has been used to synthesize nanoparticles of cobalt oxide. The particles were well characterized by transmission electron microscopy (TEM) which showed that the average diameter of the particles is around 6 nm. X-ray diffraction (XRD) studies further confirmed the formation of the spinel Co3O4. Purity of the products was detected by Fourier transform infrared spectroscopy (FTIR) combined with thermal gravimetric analysis (TG/DTG). The magnetic measurements revealed a small hysteresis loop at room temperature indicating a weak ferromagnetic nature of the synthesized Co3O4 nanoparticles. The magnetic moment of the particles was measured to be 4.27 ?eff. 2010 Elsevier B.V. All rights reserved.
Microwave-assisted synthesis and magnetic studies of cobalt oxide nanoparticles
(2011) Bhatt, A.S.; Bhat, D.K.; Tai, C.-W.; Santosh, M.S.
An efficient microwave-assisted route has been used to synthesize nanoparticles of cobalt oxide. The particles were well characterized by transmission electron microscopy (TEM) which showed that the average diameter of the particles is around 6 nm. X-ray diffraction (XRD) studies further confirmed the formation of the spinel Co3O4. Purity of the products was detected by Fourier transform infrared spectroscopy (FTIR) combined with thermal gravimetric analysis (TG/DTG). The magnetic measurements revealed a small hysteresis loop at room temperature indicating a weak ferromagnetic nature of the synthesized Co3O4 nanoparticles. The magnetic moment of the particles was measured to be 4.27 ?eff. © 2010 Elsevier B.V. All rights reserved.