  • No Thumbnail Available
    Item
    Laser surface melting of ?-TiAl alloy: An experimental and numerical modeling study
    (Institute of Physics Publishing helen.craven@iop.org, 2019) Mallikarjuna, M.; Bontha, S.; Krishna, P.; Balla, V.K.
    The objective of present work is to study the evolution of thermal stresses during laser surface melting (LSM) of ?-TiAl alloy using experimental and numerical modeling approaches. LSM of ?-TiAl alloy samples were carried out at different processing conditions in a controlled atmosphere. Material characterization of the melted region was investigated using scanning electron microscope. It was found that fully lamellar microstructure was transformed into predominantly ?-TiAl with little amount of ?2-Ti3Al. A maximum improvement in hardness of over 72% was noticed in the melted region compared to that of the substrate. Three-dimensional thermomechanical finite element analysis of LSM of ?-TiAl alloy was carried out. Melt pool dimensions, temperature history, and residual stresses were predicted from the finite element models. Measured and predicted values of melt pool depth were in good agreement with a maximum error of 13.6% at P=400Wand V=10mms-1. Predicted residual stress in the melted region exceeded the yield strength of ?-TiAl alloy and resulted in cracking of the melted region at all process conditions. ©2019 IOP Publishing Ltd.
  • No Thumbnail Available
    Item
    Prediction and validation of residual stresses generated during laser metal deposition of ? titanium aluminide thin wall structures
    (Institute of Physics Publishing helen.craven@iop.org, 2019) Mallikarjuna, M.; Bontha, S.; Krishna, P.; Balla, V.K.
    The focus of the current work is to predict and validate residual stresses developed during Laser Metal Deposition (LMD) of Gamma Titanium Aluminide (?-TiAl) alloy by using a combination of numerical modeling and experimental methods. Laser Engineered Net Shaping (LENS), which is one of the commercially available LMD techniques, was used to fabricate ?-TiAl alloy thin wall structures at various processing conditions. These deposits are expected to develop residual stresses due to the rapid heating and cooling cycles involved in the LMD process. 3D transient thermomechanical finite element analysis was used to simulate the LMD process. Thermal gradients and residual stresses were predicted from the thermomechanical models. It was found that the magnitude of thermal gradients increases with the addition of each deposited layer. Tensile residual stresses were observed at the edges of the thin-wall, while compressive residual stresses were observed at the center of the wall as well as in regions away from the edges. Residual stresses in the deposited samples were also measured using the x-ray diffraction technique. Reasonable agreement was observed between the predicted and measured values of residual stresses. © 2019 IOP Publishing Ltd.