    2-(4-(Diethylamino)-2-hydroxybenzyledene) Hydrazinecarboamide as Corrosion Inhibitor on AA2024-T3 Aluminium Alloy in 0.5 M Hydrochloric Acid Solution
    (2018) Prakashaiah, B.G.; Shetty, A.N.; Amitharani, B.E.
    A new compound 2-(4-(diethylamino)-2-hydroxybenzyledene) hydrazinecarboamide (DHBHC) was prepared by the condensation of thiosemicarbazide and diethylaminosalicyaldehyde in ethanol water mixture and its purity was confirmed with IR, H1 and C13 NMR. Anticorrosion properties of this new compound were studied on the aluminium alloy AA2024-T3 in 0.5M HCl solution at 303 K by potentiodynamic polarization, electrochemical impedance spectroscopy and weight loss method. The inhibition efficiency of DHBHC was found to increase with an increase of its concentration. The inhibition efficiency obtained in this study was 96 3% in the presence of 10 10?5 M of DHBHC. The surface morphology of the alloy was investigated both in the presence and in the absence of the inhibitor by field emission scanning electron microscopy, 3D profilometry and X-ray photoelectron spectroscopy. 2018, Allerton Press, Inc.
  • No Thumbnail Available
    Item
    2-(4-(Diethylamino)-2-hydroxybenzyledene) Hydrazinecarboamide as Corrosion Inhibitor on AA2024-T3 Aluminium Alloy in 0.5 M Hydrochloric Acid Solution
    (Pleiades Publishing compmg@maik.ru, 2018) Prakashaiah, B.G.; Nityananda Shetty, A.; Amitharani, B.E.
    A new compound 2-(4-(diethylamino)-2-hydroxybenzyledene) hydrazinecarboamide (DHBHC) was prepared by the condensation of thiosemicarbazide and diethylaminosalicyaldehyde in ethanol–water mixture and its purity was confirmed with IR, H1 and C13 NMR. Anticorrosion properties of this new compound were studied on the aluminium alloy AA2024-T3 in 0.5M HCl solution at 303 K by potentiodynamic polarization, electrochemical impedance spectroscopy and weight loss method. The inhibition efficiency of DHBHC was found to increase with an increase of its concentration. The inhibition efficiency obtained in this study was 96 ± 3% in the presence of 10 × 10?5 M of DHBHC. The surface morphology of the alloy was investigated both in the presence and in the absence of the inhibitor by field emission scanning electron microscopy, 3D profilometry and X-ray photoelectron spectroscopy. © 2018, Allerton Press, Inc.